Deep Penetration Crystal Sealer

Deep Penetration Crystal Sealer 


DPS, is the abbreviation for Deep Penetration Sealer (deep penetration crystalline waterproof material). Is the domestic national standard definition, is water-based (or water, water-based) infiltration crystalline inorganic waterproof material.

Waterproof mechanism

Its water-proof mechanism is a chemical reaction with the free base in the concrete to produce a stable dendritic crystalline colloid, which can effectively block the fine cracks and capillary voids inside the concrete, so that the concrete structure has a lasting waterproof function and better density And compressive strength. Penetration depth of 20-30mm, but also can effectively prevent the acidic substances, oil and oil erosion of concrete. Can be used in any case of concrete base.

advantage

One does not need to find leveling and protective layer, directly in the concrete layer can be sprayed 2 times, each worker can build 1000 square feet / day;

Two infiltration grade to S11 or more;

Three shelf life of more than 50 years. Not aging, deterioration;

Four can be wet construction surface construction, conservation period is very short, not afraid of rain;

Five after pouring the floor to do waterproof construction, can save a long time period;

Six completely environmentally friendly non-toxic, do pool pool and other internal walls;

Seven prices are lower than other materials.

Implementation of standards

Functional testing

JCT1018-2006 Apparent inspection (waterborne permeable crystalline waterproof material);

parameter:

JCT1018-2006

PH value: 11 ± 1;

Appearance: colorless and tasteless;

Density: 1.07 ± 0.05;

Flammability: nonflammable;

Freezing point: 0 °;

Boiling point: 100 °;

Surface tension: ≤ 36 mN / m;

Gelation time: ≤400 minutes; no initial setting;

Penetration depth: about 3 cm (strength C25 concrete);

DBJ01-01-54-2001

Compressive strength: ≥ 100%;

48 hours Water absorption: ≤ 65%;

Water resistance ratio: ≥200%;

Frost resistance: 20 ° ~ - 20 °, 15 times the surface without powder, crack;

Heat resistance: 80 °, 72 hours, the surface without powder, crack;

Alkali resistance: saturated calcium hydroxide solution soak 168 hours, the surface without powder, crack;

Acid resistance: 1% hydrochloric acid solution soak for 168 hours, the surface without powder, crack;

Reinforcement corrosion: no corrosion;

Resistance to chloride ion permeability: ≤ 1000 C;